Title:
Research on Road Performance of Dense Type Large Particle Rubber Bituminous Mixture
作者:
于艳春1 高明星2 马爱英2 侯明宇3
1. 江苏城市职业学院, 南京 210036;
2. 内蒙古农业大学能源与交通工程学院, 呼和浩特 010018;
3. 内蒙古东昊水电路桥工程有限责任公司, 内蒙古 赤峰 024000
Author(s):
YU Yan-chun1 GAO Ming-xing2 MA Ai-ying2 HOU Ming-yu3
1. The City Vocational College of Jiangsu, Nanjing 210036, China;
2. College of Energy and Transportation Engineering, Inner Mongolia Agricultural University, Hohhot 010018, China;
3. Hydropower Road and Bridge Engineering Limited Liability Company
关键词:
橡胶颗粒沥青混合料高温稳定性低温抗裂性水稳定性
Keywords:
rubber particlebituminous mixturehigh-temperature stabilitylow-temperature crack resistancewater stability
分类号:
U416.218
DOI:
-
文献标识码:
-
摘要:
通过车辙试验、浸水马歇尔试验和冻融劈裂试验、低温弯曲试验分别研究了4目、8目和12目三种橡胶颗粒粒径、不同橡胶颗粒掺量下沥青混合料的路用性能.研究结果表明:随着橡胶颗粒掺量的加大,混合料的高温稳定性能提高的幅度也越大,但橡胶颗粒的粒径对沥青混合料的高温稳定性影响并不明显.在沥青混合料中掺入橡胶颗粒掺量越多,沥青混合料的水稳定性越弱,掺入12目的橡胶颗粒对沥青混合料的水稳定性的降低影响最小.为了保证路面的抗水剥落的能力,橡胶颗粒的掺量不宜超过5%.除掺入2%的4目橡胶颗粒时情况例外,每种粒径的橡胶颗粒掺量越多,橡胶颗粒沥青混合料的低温抗裂性能越好.
Abstract:
The road performance of asphalt mixture are studied for three kinds of rubber particle size(4orders,8orders and 12orders)and different dosages through the rutting test,immersed Marshall test and freeze-thaw splitting test and low-temperature bending test,respectively.Results show that the performance of high temperature stability of the mixture is improved with the increase of dosage of rubber particles,however,the effect of rubber particle size on the high stability of the asphalt mixture is not obvious.The more adding dosage of rubber particles in asphalt mixture,the worse the water stability of asphalt mixture.The rubber particle of 12 orders has a minimal impact on the water stability of asphalt mixture.In order to guarantee the road water peeling resistance,rubber particle content should not be more than 5%.Only the condition when the asphalt mixture is mixed with 2% of the rubber particles of 4order.It shows that the more the dosage of different size of rubber particles,the better temperature crack resistance of asphalt mixture.

参考文献/References

[1] Bueno M,Luong J,Terán F,et al.Macrotexture influence on vibrational mechanisms of the tyreroad noise of an asphalt rubber pavement[J]. International Journal of Pavement Engineering,2014,15,(7):606-613.
[2] Mull M A,Stuart K,Yehia A.Fracture resistance characterization of chemically modified crumb rubber asphalt pavement[J]. Journal of Materials Science,2002,37,(3):557-566.
[3] Frédérique Guillamot,Laurent Goujard,Delphine Simard,et al.Influence of interface energy on compatibility between ground tyre rubber and bitumen used in asphalt pavement[J]. Road Materials and Pavement Design, 2013,14,(2):372-383.
[4] Xiao Feipeng,Serji N Amirkhanian,Shen Junan,et al.Influences of crumb rubber size and type on reclaimed asphalt pavement(RAP) mixtures[J]. Construction and Building Materials,2008,23,(2):1028-1034.
[5] Luong J,Bueno M,Vázquez V F,et al.Ultrathin porous pavement made with high viscosity asphalt rubber binder:A better acoustic absorption?[J]. Applied Acoustics,2014,79,:117-123.
[6] Losa,Massimo,Leandri,et al.Improvement of Pavement Sustainability by the Use of Crumb Rubber Modified Asphalt Concrete for Wearing Courses[J]. International Journal of Pavement Research and Technology,2012,5,(6):395-404.
[7] Nuha Salim Mashaan,Asim H Ali,Suhana Koting,et al.Performance Evaluation of Crumb Rubber Modified Stone Mastic Asphalt Pavement in Malaysia[J]. Advances in Materials Science and Engineering,2013(2013):1-8.
[8] 周纯秀,谭忆秋,徐立廷,等.废旧轮胎橡胶颗粒在沥青混合料中的应用[J],合成橡胶工业,2005,28,(2):81-84.
[9] 曹卫东,周海生,吕伟民.废橡胶颗粒改性沥青混合料的设计与性能[J],建筑材料学报,2005,8,(5):562-566.
[10] 张金喜.废橡胶作为弹性沥青混凝土路面材料的实验研究[J],建筑材料科学,2004,7,(4):397-404.
[11] 谭忆秋,徐立廷.马歇尔法下橡胶改性沥青混凝土成型工艺研究[J],公路,2006(2):137-139.
[12] 辛星,谭忆秋,徐立廷,等.橡胶颗粒沥青混合料设计的影响因素分析[J],公路,2006(11):161-164.
[13] 高明星,朱守林,方淑艳,等.密实型废旧橡胶颗粒沥青混合料的降噪特性研究[J],内蒙古农业大学学报:自然科学版,2009,30,(1):158-162.
[14] 高明星,徐海林,方淑艳,等.橡胶颗粒沥青混合料吸声降噪特性的研究[J],内蒙古农业大学学报:自然科学版,2010,31,(4):168-171.
[15] 周纯绣,冰雪地区橡胶颗粒沥青混合料应用技术的研究[D].哈尔滨:哈尔滨工业大学,2006.
[16] 孙娜,高明星,戴永杰,等.橡胶颗粒分布层位对沥青路面降噪效果影响的研究[J],内蒙古农业大学学报:自然科学版,2009,30,(4):201-203.
[17] 高明星,徐海林,方淑艳,等.橡胶颗粒沥青路面/轮胎噪声的有限元分析[J],内蒙古农业大学学报:自然科学版,2010,31,(3):188-192.
[18] 王志臣.干法橡胶沥青混合料动蠕变试验及黏弹性模型研究[J],内蒙古大学学报:自然科学版,2013,44,(6):647-653.
[19] 张争奇,籍晓靖,吴瑞环,等.沥青混合料轴向局部加载试验研究[J],内蒙古大学学报:自然科学版,2012,43,(6):652-659.
[20] 王昌衡,陈建民.沥青混合料车辙试验研究[J],中外公路,2003,23,(6):81-83.
[21] 孙长军,王旭东,李美江.废轮胎胶粉在公路工程中的应用及前景展望[J],橡胶科技场,2005(12):1-4.
[22] 包秀宁,李燕枫,王哲人.沥青混合料水损害试验方法探究[J],广州大学学报:自然科学版,2003,2,(2):157-159.
[23] 许涛,黄晓明.沥青混合料水损害性评价方法研究[J],公路,2003,8,(8):13-17.
[24] 中华人民共和国交通部,公路沥青路面施工技术规范(JTG F402004)[S].北京:人民交通出版社,2005:35-36.
[25] 卢铁瑞.道路沥青混合料低温性能评价指标的研究[J],石油沥青,1998,12,(1):2032,19.
[26] 张登良,沥青路面[M].北京:人民交通出版社,1999:55-75.
[27] 高明星,连续级配橡胶颗粒沥青路面降噪特性的研究[D].呼和浩特:内蒙古农业大学,2009.

备注/Memo

备注/Memo:
收稿日期:2014-6-6;改回日期:2014-1-10。
基金项目:内蒙古自治区高等学校科研项目(NJZY11060)
作者简介:于艳春(1975-),女(蒙古族),内蒙古赤峰人,讲师,博士.E-mail:Cyc0808@163.com.
通讯作者:高明星(1981-),男,内蒙古赤峰人,副教授,博士.
通讯作者:高明星(1981-),男,内蒙古赤峰人,副教授,博士.
更新日期/Last Update: 1900-01-01